- 吸水率 [%]: 4.4
- 弯曲强度 [MPa]: 0.414
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 4.4 % @Time 2.59e+6 sec | 4.4 % @Time 720 hour | immersion; cured 90 days @ 25°C | ||
| 4.4 % @Time 2.59e+6 sec | 4.4 % @Time 720 hour | immersion; cured 30 days @ 25°C | |||
| 4.9 % @Time 7200 sec | 4.9 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | |||
| 5.4 % @Time 2.59e+6 sec | 5.4 % @Time 720 hour | immersion; cured 7 days @ 25°C | |||
| Viscosity | 1390 cP | 1390 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 25 @Temperature 75.0 °C | 25 @Temperature 167 °F | cured 7 days @ 25°C | ||
| 30 @Temperature 75.0 °C | 30 @Temperature 167 °F | cured 2 hrs. @ 93°C | |||
| 32 @Temperature 25.0 °C | 32 @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| 35 @Temperature 25.0 °C | 35 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 62 @Temperature 0.000 °C | 62 @Temperature 32.0 °F | cured 7 days @ 25°C | |||
| Hardness, Shore D | 30 @Temperature 0.000 °C | 30 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | ||
| 75 @Temperature -60.0 °C | 75 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| 76 @Temperature -60.0 °C | 76 @Temperature -76.0 °F | cured 7 days @ 25°C | |||
| Tensile Strength, Ultimate | 0.414 MPa | 60.0 psi | cured 7 days @ 25°C | ||
| 0.448 MPa | 65.0 psi | cured 30 days @ 25°C | |||
| 0.483 MPa | 70.0 psi | cured 90 days @ 25°C | |||
| 0.517 MPa | 75.0 psi | cured 2 hours @ 93°C | |||
| Elongation at Break | 150 % | 150 % | cured 2 hours @ 93°C | ||
| 155 % | 155 % | cured 90 days @ 25°C | |||
| 175 % | 175 % | cured 30 days @ 25°C | |||
| 190 % | 190 % | cured 7 days @ 25°C | |||
| Shear Strength | 1.45 MPa @Temperature 25.0 °C | 210 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 30 days @ 25°C | ||
| 2.07 MPa @Temperature 0.000 °C | 300 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | |||
| 2.14 MPa @Temperature 25.0 °C | 310 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 90 days @ 25°C | |||
| 3.76 MPa @Temperature 25.0 °C | 545 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.30e+9 ohm-cm @Temperature 25.0 °C | 1.30e+9 ohm-cm @Temperature 77.0 °F | cured 30 days @ 25°C | ||
| 2.30e+9 ohm-cm @Temperature 25.0 °C | 2.30e+9 ohm-cm @Temperature 77.0 °F | cured 90 days @ 25°C | |||
| 3.20e+9 ohm-cm @Temperature 25.0 °C | 3.20e+9 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| 4.90e+9 ohm-cm @Temperature 25.0 °C | 4.90e+9 ohm-cm @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 70 min @Temperature 25.0 °C | 70 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-1 | |||
| 8.5 | AboCure 8110-3 | ||||