- 拉伸强度 [MPa]: 16.5
- 脆化温度 [℃]: -59.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | |||
| Mooney Viscosity | 70 @Temperature 100 °C | 70 @Temperature 212 °F | ML 1+4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 62 | 62 | aged 70 hours at 250ºF | ||
| 62 | 62 | aged 70 hours at 300ºF | |||
| 66 | 66 | aged 7 days at Room Temp in ASTM Fuel A | |||
| 66 | 66 | aged 70 hours at 250ºF in ASTM Oil #903 | |||
| 66 | 66 | aged 96 hours at 158ºF | |||
| 66 | 66 | ||||
| 67 | 67 | aged 7 days at Room Temp in ASTM Fuel B | |||
| 67 | 67 | aged 70 hours at 250ºF in ASTM Oil #901 | |||
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | aged 7 days at Room Temp in ASTM Fuel B | ||
| 21.0 MPa | 3050 psi | aged 70 hours at 300ºF | |||
| 22.8 MPa | 3300 psi | aged 70 hours at 250ºF in ASTM Oil #901 | |||
| 23.4 MPa | 3400 psi | aged 70 hours at 250ºF in ASTM Oil #903 | |||
| 25.9 MPa | 3750 psi | aged 7 days at Room Temp in ASTM Fuel A | |||
| 27.2 MPa | 3950 psi | aged 70 hours at 250ºF | |||
| 29.0 MPa | 4200 psi | ||||
| 29.3 MPa | 4250 psi | aged 96 hours at 158ºF | |||
| Elongation at Yield | 300 % | 300 % | aged 7 days at Room Temp in ASTM Fuel B | ||
| 370 % | 370 % | aged 7 days at Room Temp in ASTM Fuel A | |||
| 400 % | 400 % | ||||
| 410 % | 410 % | aged 70 hours at 250ºF in ASTM Oil #903 | |||
| 420 % | 420 % | aged 70 hours at 250ºF in ASTM Oil #901 | |||
| 420 % | 420 % | aged 70 hours at 250ºF | |||
| 470 % | 470 % | aged 96 hours at 158ºF | |||
| 490 % | 490 % | aged 70 hours at 300ºF | |||
| 100% Modulus | 0.00352 GPa | 0.510 ksi | |||
| 200% Modulus | 0.00979 GPa | 1.42 ksi | |||
| 300% Modulus | 0.0121 GPa | 1.75 ksi | aged 70 hours at 300ºF | ||
| 0.0156 GPa | 2.26 ksi | aged 70 hours at 250ºF in ASTM Oil #901 | |||
| 0.0157 GPa | 2.28 ksi | aged 70 hours at 250ºF in ASTM Oil #903 | |||
| 0.0165 GPa | 2.40 ksi | aged 7 days at Room Temp in ASTM Fuel B | |||
| 0.0179 GPa | 2.60 ksi | aged 70 hours at 250ºF | |||
| 0.0185 GPa | 2.68 ksi | aged 96 hours at 158ºF | |||
| 0.0186 GPa | 2.70 ksi | aged 7 days at Room Temp in ASTM Fuel A | |||
| 0.0190 GPa | 2.75 ksi | ||||
| Tear Strength | 550 kN/m | 3140 pli | ASTM Die C | ||
| Compression Set | 20 % @Temperature 70.0 °C, Time 79200 sec | 20 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -59.0 °C | -74.2 °F | Bell | ||
| Descriptive Properties | |||||
| Bashore Resilience (%) | 47 | ||||
| Gehman Modulus (ºC) | -25.5 | T2 | |||
| -33.1 | T5 | ||||
| -35 | T10 | ||||
| -39.5 | T100 | ||||
| Mooney Scorch | 25 | t5, minutes; MS @ 121ºC | |||
| Temperature of Retraction (ºC) | -11 | TR-50 | |||
| -23.7 | TR-30 | ||||
| -3.4 | TR-70 | ||||
| -33.4 | TR-10 | ||||
| Volume Change (%) | -0.67 | aged 70 hours at 250ºF in ASTM Oil #901 | |||
| -1.03 | aged 70 hours at 250ºF in ASTM Oil #903 | ||||
| 1.3 | aged 7 days at Room Temp in ASTM Fuel A | ||||
| 16 | aged 7 days at Room Temp in ASTM Fuel B | ||||