- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.80 MPa | 1712 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.5 MPa | 1810 psi | ASTM D882 |
| Film Elongation at Break, MD | 595 % | 595 % | ASTM D882 |
| Film Elongation at Break, TD | 652 % | 652 % | ASTM D882 |
| Secant Modulus, MD | 0.221597 GPa | 32.1405 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.257526 GPa | 37.3516 ksi | 2% Secant; ASTM D882 |
| Impact | 24 | 24 | [lbf]; Puncture Resistance Force; Dow Method |
| 249 | 249 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| Puncture Energy | 9.04 J | 6.67 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 707 g | 707 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1033 g | 1033 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.92 g/micron | 353.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.33 g/micron | 516.5 g/mil | ASTM D1922 |
| Dart drop Test | 780 g | 1.72 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 57.27 MPa | 8307 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.47 MPa | 7755 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 106 °C | 223 °F | 2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 67 % | 67 % | 45°; ASTM D2457 |