- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 1.1
- 断裂伸长率 [%]: 265
- 弯曲强度 [MPa]: 175.0
- 弯曲模量 [MPa]: 8.40
- 热变形温度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.4 % | 6.4 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM data MD |
| 0.013 cm/cm | 0.013 in/in | ISO data | |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 175 MPa | 25400 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 2.8 % | 2.8 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 265 MPa | 38400 psi | ASTM Data |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO Value |
| 9.38 GPa | 1360 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.0 µm/m-°C @Temperature 20.0 °C | 21.1 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO data |
| 208 °C | 406 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 °C | 500 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |