- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 7.3
- 拉伸强度 [MPa]: 48.0
- 断裂伸长率 [%]: 65.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.69
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.3 % | 7.3 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO value at 50 mm/min. |
| 50.0 MPa | 7250 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO data, 50 mm/min |
| >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min | |
| Tensile Modulus | 1.84 GPa | 267 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | ASTM Data |
| Flexural Modulus | 1.69 GPa | 245 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 0.700 GPa | 102 ksi | calculated |
| Charpy Impact, Notched | NB | NB | ISO Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM Data |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |