- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.5
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 1.90
- 硬度: 82.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 82 | 82 | ASTM Test | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM Test | ||
| 100 MPa @Temperature -40.0 °C | 14500 psi @Temperature -40.0 °F | ASTM Test | |||
| 100 MPa @Temperature -40.0 °C | 14500 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527 | ||
| 65.0 MPa | 9430 psi | 2 in/min; ASTM Test | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ISO Data | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ASTM Test | |||
| 25.0 MPa @Temperature 80.0 °C | 3630 psi @Temperature 176 °F | ASTM Test | |||
| 25.0 MPa @Temperature 80.0 °C | 3630 psi @Temperature 176 °F | ISO Data | |||
| 117 MPa @Temperature -40.0 °C | 17000 psi @Temperature -40.0 °F | ASTM Test | |||
| 117 MPa @Temperature -40.0 °C | 17000 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | 40 % | 40 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| 9.0 % @Temperature -40.0 °C | 9.0 % @Temperature -40.0 °F | ASTM Test | |||
| 9.0 % @Temperature -40.0 °C | 9.0 % @Temperature -40.0 °F | ISO Data | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM Test | |||
| 7.0 % @Temperature -40.0 °C | 7.0 % @Temperature -40.0 °F | ASTM Test | |||
| 7.0 % @Temperature -40.0 °C | 7.0 % @Temperature -40.0 °F | ISO Data | |||
| 29 % @Temperature 80.0 °C | 29 % @Temperature 176 °F | ISO Data | |||
| 29 % @Temperature 80.0 °C | 29 % @Temperature 176 °F | ASTM Test | |||
| 34 % @Temperature 120 °C | 34 % @Temperature 248 °F | ASTM Test | |||
| 34 % @Temperature 120 °C | 34 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 2.30 GPa | 334 ksi | 1mm/min; ISO 527 | ||
| 0.295 GPa @Temperature 120 °C | 42.8 ksi @Temperature 248 °F | ISO Data | |||
| 0.400 GPa @Temperature 80.0 °C | 58.0 ksi @Temperature 176 °F | ISO Data | |||
| 2.84 GPa @Temperature -40.0 °C | 412 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 65.0 MPa | 9430 psi | ISO Data | ||
| 87.0 MPa | 12600 psi | ASTM Test | |||
| 14.0 MPa @Temperature 120 °C | 2030 psi @Temperature 248 °F | ASTM Test | |||
| 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | ASTM Test | |||
| 25.0 MPa @Temperature 65.0 °C | 3630 psi @Temperature 149 °F | ASTM Test | |||
| 148 MPa @Temperature -40.0 °C | 21500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO Data | ||
| 2.21 GPa | 321 ksi | ASTM Test | |||
| 0.260 GPa @Temperature 120 °C | 37.7 ksi @Temperature 248 °F | ASTM Test | |||
| 0.325 GPa @Temperature 93.0 °C | 47.1 ksi @Temperature 199 °F | ASTM Test | |||
| 0.415 GPa @Temperature 65.0 °C | 60.2 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.800 J/cm @Temperature -40.0 °C | 1.50 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.48 J/cm @Thickness 3.17 mm | 2.77 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 | ||
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 88.0 µm/m-°C | 48.9 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C | 51.7 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 | ||
| 168 °C | 334 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 | ||
| 60.0 °C | 140 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||