- 密度 [g/cm3]: 1.26
- 缺口冲击强度: 2.56
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| 1.263 g/cc | 0.04563 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0011 cm/cm @Time 86400 sec | 0.0011 in/in @Time 24.0 hour | ISO 294 |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec | 0.0010 - 0.0020 in/in @Time 24.0 hour | ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0062 cm/cm @Time 86400 sec | 0.0062 in/in @Time 24.0 hour | ISO 294 |
| 0.0060 - 0.0070 cm/cm @Time 86400 sec | 0.0060 - 0.0070 in/in @Time 24.0 hour | ASTM D 955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| 134 MPa | 19400 psi | ASTM D 638 | |
| Elongation at Break | 6.2 % | 6.2 % | ASTM D 638 |
| 6.3 % | 6.3 % | ISO 527 | |
| Tensile Modulus | 7.08 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| 7.37 GPa | 1070 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 193 MPa | 28000 psi | ISO 178 |
| 195 MPa | 28300 psi | ASTM D 790 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
| 6.64 GPa | 963 ksi | ISO 178 | |
| Izod Impact, Notched | 2.56 J/cm @Temperature 23.0 °C | 4.80 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 14.31 J/cm @Temperature 23.0 °C | 26.81 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² @Temperature 23.0 °C | 41.4 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 16.0 J @Temperature 23.0 °C | 11.8 ft-lb @Temperature 73.4 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 34.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 19.1 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 34.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 19.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 99.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 99.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 178 °C @Thickness 3.20 mm | 352 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |